Investigation of microstructure and wear properties of Al–4.5 wt.% TiC nanocomposites produced by mechanical milling
Publish place: Iran International Aluminum Conference
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,157
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC02_024
تاریخ نمایه سازی: 12 اردیبهشت 1392
Abstract:
The present work deals with studies on the manufacturing and investigation of mechanical and wear behavior of aluminum alloy matrix composites (AAMCs), produced using powder metallurgy technique of ball milled mixing in a high energy attritor and using a blend–press–sinter methodology. Matrix of pre-mechanical alloyed Al–4.5 wt.% Cu was used to which different fractions of nano and micron size TiC reinforcing particles (ranging from 0 to 10 wt.%) were added. The powders were mixed using a planetary ball mill. Consolidation was conducted by uniaxial pressing at 650 MPa. Sintering procedure was done at 400 ˚C for 90 min. The results indicated that as TiC particle size is reduced to nanometre scale and the TiC content is increased up to optimum levels. The wear resistance of the composite increase significantly, whereas relative density, grain size and distribution homogeneity decrease. Microstructural characterization of the as-pressed samples revealed reasonably uniform distribution of TiC reinforcing particulates and presence of minimal porosity. The weartestdisclosed that the wear resistance of all specimens increases with the addition of nano and micronsize TiCparticles (up to 5 wt.%). Scanning electron microscopic observation of the worn surfaces was conducted and the dominant wear mechanism was recognized as abrasive wear accompanied by some delamination wear mechanism.
Keywords:
Authors
Narguess Nemat
Center of Excellence for High Performance Materials, School of Metallurgy and Materials, University of Tehran, Tehran, Iran.
Massoud Emamy
Center of Excellence for High Performance Materials, School of Metallurgy and Materials, University of Tehran, Tehran, Iran.
Rasul Azari Khosroshahi
Materials Engineering Department of Sahand University of Technology (SUT), Tabriz, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :