Parya Khalatbarimohseni - Department of Medicinal Chemistry, Faculty of Pharmacy, Tehran Medical Sciences, Islamic Azad University, Tehran, Iran
Mohammad Jalali Sarvestani - Department of Chemistry, faculty of Pharmaceutical chemistry, Tehran Medical sciences, Islamic Azad university, Tehran, Iran
Shahin Ahmadi - Department of Chemistry, faculty of Pharmaceutical chemistry, Tehran Medical sciences, Islamic Azad university, Tehran, Iran
Mohammad Mahboubi-Rabbani - Department of Medicinal Chemistry, Faculty of Pharmacy, Tehran Medical Sciences, Islamic Azad University, Tehran, Iran

In this research, a coated graphite polyvinyl chloride (PVC) membrane electrode was fabricated for the potentiometric determination of lithium based on ۱۳-(۳-nitrophenyl)-۱۲H,۱۴H-benzo[g]chromeno[۲,۳-b]chromene-۷,۱۲,۱۴(۱۳H)-trione (L) as the ionophore. The best Nernstian response was observed from the membrane composition of ۳۱% PVC, ۷% L, ۲% NaTPB, and ۶۰% dioctyl phthalate (DOP) as the plasticizer. The designed sensor showed a wide linearity over the concentration range of ۱×۱۰-۸-۱×۱۰-۳ mol L-۱ with the slope of ۶۰.۲±۰.۳ mV decade-۱, and the limit of detection (LOD) of ۷.۵×۱۰-۹ mol L-۱. The selectivity of the designed sensor was investigated by matched potential method and no serious interference was observed. The response time and life span of the electrode were ۵s and ۱۶ weeks, respectively. The potential response of the electrode was independent of solution pH in the pH range of ۳.۰-۱۲.۰. The influence of the presence of organic solvents on the potential response of the electrode was also scrutinized, and the results showed that the designed sensor keeps its Nernstian behavior in solutions with ۲۰% non-aqueous content. At the end, the electrode was successfully applied to determine lithium carbonate in tablet, urine and serum samples with the recovery% values of ۹۶.۰ to ۱۰۶.۳۳ and RSD% ۱.۹۹-۴.۴۵.

Ion selective electrode, Potentiometry, Lithium carbonate, PVC membrane, Sensor, Chromene