The research aimed to create a composite material for the floaters used in floating solar power plants. High-density polyethylene (HDPE) was combined with ۱, ۱.۵, ۲, and ۲.۵% of carbon black (CB) and ۱,۲,and ۳% of zinc oxide (ZnO). Mechanical tests were carried out after accelerated weathering for ۳۱۱, ۶۳۴, ۹۵۴, ۱۴۰۳, and ۲۸۷۸ hours in dry (out of water) and wet (sample floating in water) conditions. HDPE loses tensile strength, impact resistance, and elongation at break after ۶۳۴ hours and ۹۵۴ hours of weathering. The Shore D hardness did not show any significant change. The best performance was observed in batches D۴ and W۴, which contain ۲% CB and ۱% ZnO, in dry and wet conditions. The SEM (scanning electron microscope) shows the external morphology of D۱ and W۱ (pure HDPE) and D۴ and W۴ (composite) and revealed that pure HDPE was more degraded compared to the composite. Thermal properties and stability were analyzed using TGA (Thermogravimetric analysis). A further increase in CB and ZnO will reduce the strength of the composite.It was found that HDPE with ۲% CB and ۱% ZnO was a good composite material for developing the floaters used in floating solar power plants.

Virgin High-Density Polyethylene (HDPE), Carbon black (CB), Zinc Oxide (ZnO), Accelerated weathering, Floating solar power plant