The Effect of ۶۰% Cold Rolling on the Microstructure and Mechanical Properties of the High Entropy Alloy AlCoCrFeNi۲.۱
عنوان مقاله: The Effect of ۶۰% Cold Rolling on the Microstructure and Mechanical Properties of the High Entropy Alloy AlCoCrFeNi۲.۱
شناسه ملی مقاله: JR_IJMF-11-1_003
منتشر شده در در سال 1403
شناسه ملی مقاله: JR_IJMF-11-1_003
منتشر شده در در سال 1403
مشخصات نویسندگان مقاله:
A. Chehri - Department of Mechanical Engineering, Kermanshah Branch, Islamic Azad University, Kermanshah, Iran
A. Adelkhani - Department of Mechanical Engineering, Kermanshah Branch, Islamic Azad University, Kermanshah, Iran
M. Seifpour Bijnavand - Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran
خلاصه مقاله:
A. Chehri - Department of Mechanical Engineering, Kermanshah Branch, Islamic Azad University, Kermanshah, Iran
A. Adelkhani - Department of Mechanical Engineering, Kermanshah Branch, Islamic Azad University, Kermanshah, Iran
M. Seifpour Bijnavand - Department of Materials and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran
High entropy alloys are a new class of materials that have attracted much attention due to their attractive properties. High entropy alloys have various types and structures, among which, eutectic high entropy alloys have received much attention due to their unique characteristics. In this study, the effect of ۶۰% cold rolling on the properties of AlCoCrFeNi۲.۱ eutectic high entropy alloy is investigated and compared with the casting condition. This alloy shows a layered structure consisting of FCC and BCC phases in both as-cast and cold-alloyed samples. In the as-cast state, the alloy showed a hardness of ۳۵۲ Vickers, which increased to ۴۰۱ Vickers following a ۶۰% cold rolling. To further investigate the mechanical properties, both samples were subjected to a shear-punch test (SPT). According to the results, the as-cast sample shows good flexibility and strength which has subsequently risen following cold rolling. The measured values of the yield shear strength and final shear strength for as cast and ۶۰% cold-rolled samples are ۲۰۴, ۲۶۹, ۲۹۴, and ۳۱۷, respectively.
کلمات کلیدی: High entropy alloys, eutectic high entropy alloy, hardness, shear-punch test (SPT)