In this study, bismuth titanate (BIT) powder was synthesized using the solid-state synthesis method. The effect of zinc oxide (ZnO) nanoparticles as a sintering aid on the electrical properties of BIT ceramic was then investigated. The weight percentages of ZnO used were ۰.۳, ۰.۶, and ۱.۲. Disc-shaped samples were prepared using the uniaxial pressing method and sintered at temperatures of ۱۰۲۵, ۱۰۷۵, and ۱۱۲۵ °C for durations of ۱, ۲, and ۵ h, and with heating rates of ۳, ۵, and ۱۰ °C/min. The highest density values were achieved under the optimal sintering conditions of ۱۰۷۵ °C, ۲ h, and a heating rate of ۵ °C/min. The addition of ZnO nanoparticles improved the densification of BIT ceramic. In the sample containing ۱.۲ wt.% of ZnO, a secondary phase of Zn۲TiO۴ was identified. The inclusion of ZnO nanoparticles resulted in an increase in the dielectric constant, a reduction in dielectric loss, and improvements in the piezoelectric and ferroelectric properties of BIT ceramics. These enhancements contributed to increased density and reduced electrical conductivity. The best results were obtained with the sample containing ۰.۶ wt.% of nano ZnO, which exhibited a high dielectric constant (۳۱۲), low dielectric loss (tanδ = ۰.۰۱), high piezoelectric coefficient (d۳۳ = ۲۱ pC/N), and high remnant polarization (۴.۲۵ μC/cm۲).

Bismuth titanate, Zinc oxide nanoparticles, Sintering, Dielectric properties, Microstructure