In the presence of H2S, metals, such as carbon and low alloy steels, may suffer hydrogen damage and hydrogen embrittlement. If the amount of H2S in gas was high the risk of brittle failure could be increased due to the effect of internal hydrogen absorption on steel toughness. In this paper the influence of hydrogen on mechanical properties of two pipeline materials, X65 and X70 micro-alloyed, was investigated. An electrochemical hydrogen charging method has been setup. Diffusible hydrogen content of steels was in the range of 0.6 to 7.5 ppm. Charpy and stress-strain curves of tensile tests were carried out in room temperature at different charging condition .Hydrogen affects mechanical properties of the tested materials, mainly reducing fracture toughness in tensile tests, while little influence has been observed in Charpy tests. Fracture surface confirmed the results of mechanical tests.

Hydrogen charging; Stress corrosion Cracking; Pipeline Steels; Slow Strain Rate Test