Effect of Agro-Waste Ash on Mechanical Properties of Epoxy Polymer Concrete
Publish place: Iranica Journal of Energy and Environment، Vol: 4، Issue: 3
Publish Year: 1392
نوع سند: مقاله ژورنالی
زبان: English
View: 945
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJEE-4-3_015
تاریخ نمایه سازی: 1 اردیبهشت 1393
Abstract:
This paper focuses on addition of fillers in epoxy resin and aggregate for polymer concrete (PC) preparation. For the preparation of PC, two kinds of fillers, i.e. rice husk ash and broom stem ash were used.According to experimental results, addition of fillers had a positive impact on the physical and mechanical properties of the PC. In the PC sample with rice husk ash, with the filler/aggregate ratio of 0.075 and 18.4% polymer, maximum compressive strength of 86.41 Mpa was obtained; while the compressive strength of the polymer concrete without filler was 71.2 Mpa. The PC sample with broom stem ash, with the filler/aggregate ratio of 0.12 and 23% polymer showed the maximum flexural strength
Keywords:
Aggregate /Flexural strength/ Compressive strength/ Filler /Polymer concrete/ Epoxy resin
Authors
m Hoseinzadeh
Department of Civil Engineering, Nour Branch,Islamic Azad University, Nour, Iran
G.D Najafpour
School of Chemical Engineering, College of Engineering,Babol Noshirvani University of Technology, Babol, Iran
M.A Beygi
School of Civil Engineering, College of Engineering,Babol Noshirvani University of Technology, Babol, Iran