Permeation properties of a graded structure composite ceramic membrane prepared by CVD method
Publish place: 07th International Congress on Chemical Engineering
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 680
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_133
تاریخ نمایه سازی: 25 فروردین 1394
Abstract:
Permeation properties of a hydrogen permselective ceramic membrane for single gases (H2, CH4, N2 and CO2) have been studied. The membrane was prepared by depositing a thin layer of SiO2 onthe inner side of a tubular modified alumina layer by chemical vapor deposition (CVD) method.The modification process was carried out by coating the macroporous α-alumina substrate with different layers of γ-alumina to obtain a graded structure support. XRD, SEM and EDAX analysis were used to characterize the membrane. Cross-sectional and surface images obtained from SEMshowed that the intermediate layer had a thickness of 2 μm with a median pore size of about 50 nm and the top selective silica layer was uniform and dense with a thickness of about 100 nm. Permeation tests showed that H2 permeation flux reduced from 5*10-5 molm-2s-1pa-1 to 6*10-7 molm-2s-1pa-1 as the CVD deposition time proceeded from 0 to 6 h and H2 selectivities over CH4, N2 and CO2 increased from 2.2, 5.6 and 7.9 to 105, 178 and 446, respectively
Keywords:
Authors
Ensieh Ganji Babakhani
Research Institue of Petroleum Industry,Tehran,Iran
Mahdi Amanipour
Sharif University of Technology,Tehran,Iran
Aliakbar Safe kordi
Sharif University of Technology,Tehran,Iran
Akbar Zamaniyan
Research Institue of Petroleum Industry,Tehran,Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :