Thermal Catalytic Cracking of Naphtha over CeO2 Supported on Multi Wall Carbon Nanotubes Coated with SiO2
عنوان مقاله: Thermal Catalytic Cracking of Naphtha over CeO2 Supported on Multi Wall Carbon Nanotubes Coated with SiO2
شناسه ملی مقاله: ICHEC07_362
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال 1390
شناسه ملی مقاله: ICHEC07_362
منتشر شده در هفتمین کنگره ملی مهندسی شیمی در سال 1390
مشخصات نویسندگان مقاله:
Somaye Sheybani - Department of Chemical Engineering, Tarbiat Modares University
Jafar Towfighi - Department of Chemical Engineering, Tarbiat Modares University
Ali Mohamadalizade - Gas Research Division, Research Institute of Petroleum Industry
خلاصه مقاله:
Somaye Sheybani - Department of Chemical Engineering, Tarbiat Modares University
Jafar Towfighi - Department of Chemical Engineering, Tarbiat Modares University
Ali Mohamadalizade - Gas Research Division, Research Institute of Petroleum Industry
In this research Multi wall Carbon Nanotubes (MWNTs) were coated first with SiO2 and then decorated with CeO2 nano particles and vice versa. The effect of metal oxide deposition priority on increasing the thermal resistance of MWNTs was investigated and results indicated the best performance for catalyst which was coated first with CeO2. Catalysts were caracterized with XRD, SEM, TGA,and ASAP. The Performance of catalysts in thermal catalytic cracking (TCC) of naphta for production of light olefins was studied at 680oC and the steam ratio equal to 0.5; finally the results were compared with thermal cracking conditions