Abstract:
Ag/TiO2 coating was prepared by anodizing the surface of Ti followed by electrodeposition of silver. By X-ray diffraction (XRD) analyses, that indicated thecrystalline size of Ag deposit onto the oxidized surface of Ti was around 32 nm. Scanning electron microscopy (SEM) images of the oxidized surface with and without Ag deposit show that TiO2 is formed uniformly but Ag deposit consisted of numerous spherical structures. The results of in vitro test showed Ag/TiO2 coating is biocompatible
Keywords:
Authors
Mojdeh Azizi
Master of Materials Engineering, Shiraz University
Rahmat Allah Emadi
Professor in Department of Materials Engineering, Isfahan University of Technology
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :