Effect of heat treatment on adhesion strength of clear coatings in beech and poplar wood
Publish place: 6th International Color & Coating Congress
Publish Year: 1394
نوع سند: مقاله کنفرانسی
زبان: English
View: 575
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCC06_280
تاریخ نمایه سازی: 25 بهمن 1394
Abstract:
The aim of this study was to investigate the influence of heat treatment of wood on adhesion strength of clear coatings. For this purp ose, specimens of beech and poplar wood with dimensions of 20×100×150 mm3 prepared. Heat treatments were performed in 160 and 180 °C for 3 hours in dry condition. Surface of treated and untreated specimens were covered with clear coatings in three separate processes: 1. sealer-acid catalyzed lacquer, 2.polyurethane and 3. Special coating of thermowood. After applying the coating, the adhesion strength (Pull-off) and scratch (Cross-Cut) were measured and compared to untreated specimens. Resu lts showed that by increasing the temperature of heat treatment, adhesion strength reduced. The reduction in polyurethane coating and sealer-acid catalyzed lacquer was statistically significant. The adhesion strength of coating in the Beech wood was higher than poplar wood. The best adhesion strength observed in polyurethane coating and the lowest quantity was obtained in sealer-acid catalyzed coating.
Keywords:
Adhesion strength- Clear Coatings- Heat treatment- Beech- Poplar
Authors
A. Talaei
Wood Science and Technology, Faculty of Civil Engineering, University of Shahid Rajaee Teacher Training, Tehran, Iran.
M. Saleh Zare
Department of Wood Science and Technology, Faculty of Civil Engineering, University of Shahid Rajaee Teacher Training, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :