Influence of polyaniline nanoparticles on the corrosion protection properties of epoxy nanocomposite coating
Publish Year: 1393
نوع سند: مقاله کنفرانسی
زبان: English
View: 785
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CBGCONF02_284
تاریخ نمایه سازی: 9 فروردین 1395
Abstract:
In this study the anticorrosive properties of an epoxy coating loaded with polyaniline nanoparticles is investigated by means of Electrochemical Impedance Spectroscopy (EIS) and accelerated salt spray test. The blank epoxy coating was loaded with 0.1 wt % PAni nanoparticles. Through the monitoring of open circuit potential, an ennoblement effect was detected for the systems in the presence of a 3.5 wt.% NaCl solution. Also, an increase in the impedance at low frequency range was occurred by adding polyaniline nanoparticles. The OCP and EIS results indicate that possibly a passive layer formed on the substrate surface. In addition the coating with polyaniline nanoparticles had better performance to salt spray media.
Keywords:
Authors
Ahmad Ghasemi-Kahrizsangi
Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163,Tehran, Iran
Jaber Neshati
Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163,Tehran, Iran
Homeira Shariatpanahi
Coating Research Center, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745- 4163, Tehran, Iran
Esmaeil Akbarinezhad
Coating Research Center, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745- 4163, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :