Investigation of Microstructure and Mechanical Properties of Al/nano-Al2O3 Composites Fabricated by ARB Process
عنوان مقاله: Investigation of Microstructure and Mechanical Properties of Al/nano-Al2O3 Composites Fabricated by ARB Process
شناسه ملی مقاله: IIAC03_061
منتشر شده در سومین کنفرانس بینالمللی آلومینیوم ایران IIAC2014 در سال 1393
شناسه ملی مقاله: IIAC03_061
منتشر شده در سومین کنفرانس بینالمللی آلومینیوم ایران IIAC2014 در سال 1393
مشخصات نویسندگان مقاله:
s Biabangard Barani - Department of Materials Science and Engineering, Faculty of Engineering, Ferdowsi University of Mashhad P.O. Box 91775-1111, Mashhad, Iran
s.a Sajjadi - Department of Materials Science and Engineering, Faculty of Engineering, Ferdowsi University of Mashhad P.O. Box 91775-1111, Mashhad, Iran
خلاصه مقاله:
s Biabangard Barani - Department of Materials Science and Engineering, Faculty of Engineering, Ferdowsi University of Mashhad P.O. Box 91775-1111, Mashhad, Iran
s.a Sajjadi - Department of Materials Science and Engineering, Faculty of Engineering, Ferdowsi University of Mashhad P.O. Box 91775-1111, Mashhad, Iran
In the current study the accumulative roll bonding (ARB) process was used for manufacturing Al/nanoAl2O3 composites. For this purpose Al 1050 powder was first milled with nano Al2O3 particles to produce nano composite powders. The powders were added between two Al strip and ARB process was applied to produce Al/nanoAl2O3 composite. The process was repeated up to nine passes. The resulting microstructures and thecorresponding mechanical properties of composites after different passes of ARB process were studied by optical and electron microscopy, hardness and tensile tests. The produced MMC by nine ARB cycles showed a homogeneous distribution of nano particles in the aluminum matrix. Moreover, when the number of ARB cycles was increased, up to the cycle five, the tensile strength of composite strips was decreased and then by increasing the number of cycles, the tensile strength of composite strips was increased
کلمات کلیدی: Accumulative roll bonding, nano-composite, microstructure, hardness, tensile strength