Preparation of Polymeric Membrane for pervaporation separation
Publish place: 5th International Congress on Chemical Engineering
Publish Year: 1386
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,530
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC05_182
تاریخ نمایه سازی: 7 بهمن 1386
Abstract:
Poly (ether-block-amide) membranes were made via casting a solution on a non solvent surface. In this research, effects of different parameters such as ratio of solvent mixture (n-butanol / iso propanol), temperature and polymer concentration, on quality of the thin film membranes were studied. The results showed that the film quality enhances with increasing iso propanol ratio in the solvent mixture. This behavior can be related to reduction of solution surface tension and interfacial tension between solution and non solvent. Uniform films were made at a temperature rang of 70-80 0C and a polymer concentration of 4-7 wt%. Morphology of the membrane was investigated with Scanning Electronic Micrograph (SEM). Pervaporation of ethyl butyrate / water and iso propanol / water mixtures was studied using these membranes and high separation performance was achieved. For ethyl butyrate / water mixtures, It was observed that both permeation flux and separation factor increase with increasing ethyl butyrate content in the feed. However, for iso propanol / water mixtures, it was found that by increasing iso propanol content in the feed, permeation flux enhances but separation factor diminishes. Increasing temperature in limited range studied resulted in decreasing separation factor and increasing permeation flux.
Keywords:
Authors
kikhavandi
Research Lab for Separation Processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran
Mohammadi
Research Lab for Separation Processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran
Moghbeli
Research Lab for Separation Processes, Faculty of Chemical Engineering, Iran University of Science and Technology, Narmak, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :