Improvement the Corrosion Resistance of Cr / Ni Alloy ElectroplatingCoatings in 3.5% NaCl Solution With Chemical Activation of substrate
عنوان مقاله: Improvement the Corrosion Resistance of Cr / Ni Alloy ElectroplatingCoatings in 3.5% NaCl Solution With Chemical Activation of substrate
شناسه ملی مقاله: ICRSIE01_005
منتشر شده در کنفرانس بین المللی پژوهش در علوم و مهندسی در سال 1395
شناسه ملی مقاله: ICRSIE01_005
منتشر شده در کنفرانس بین المللی پژوهش در علوم و مهندسی در سال 1395
مشخصات نویسندگان مقاله:
S. M. Madani - Graduate student of Materials Engineering, Department of Materials Engineering, Foolad Institute ofTechnology, Esfahan, Iran ,
A. Shafyei - Associate Professor of Materials Engineering, Department of Materials Engineering, Foolad Institute ofTechnology, Esfahan, Iran
A. Najafizadeh - Professor of Materials Engineering, Department of Materials Engineering, Foolad Institute of Technology,Esfahan, Iran
خلاصه مقاله:
S. M. Madani - Graduate student of Materials Engineering, Department of Materials Engineering, Foolad Institute ofTechnology, Esfahan, Iran ,
A. Shafyei - Associate Professor of Materials Engineering, Department of Materials Engineering, Foolad Institute ofTechnology, Esfahan, Iran
A. Najafizadeh - Professor of Materials Engineering, Department of Materials Engineering, Foolad Institute of Technology,Esfahan, Iran
The overall objective of this study is selecting an optimal method for the production ofchromium/ nickel coatings to reduce the density and permeability of the surface cracksand provide good corrosion resistance. For this purpose, Cr and Ni electrodeposited fromCr(III) - Ni(II) bath on St-12 steel samples by using pulse current, according to theselective three methods. The microstructures of the coatings were studied by opticalmicroscopy (OM) and scanning electron microscopy (FESEM). The coating corrosionresistance has been compared through electrochemical polarization in a 3.5% NaClsolution. Despite the high corrosion resistance for all three types of coatings; It also looksat the use of pulse current: corrosion resistance of multilayer alloy coatings are higherthan double layer, and corrosion resistance of double layer alloy coatings are higher thanthe single layer At the same thickness
کلمات کلیدی: Electroplating, Chromium, Nickel, Corrosion, Crack