FABRICATION AND EVALUATION OF STRUCTURAL PROPERTIES OF NANOCRYSTALLINE NiTiC POWDER
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 484
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_235
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
NiTiCu powders with nanocrystalline structure were successfully synthesized through mechanical alloying and subsequent heat treatment process in this research. The X-ray diffraction (XRD) analysis was revealed that after 60 h.milling of high purity elemental powders mixture of Ni, Ti and Cuvia a planetary high energy ball milling with different Cu compositions, the Cu dissolved into B2 structure and NiTi phase was obtained. Annealing of as-milled powders at 1173 K for 15 min leads to formation of nanometric NiTiCu and Ti2Ni phases, grain growth and release of internal strain. Structural characterization was examined by means of scanning electron microscopy (SEM) technique. The results demonstrated that this route result in preparation compounds with suitable morphology and homogeneous structure.
Keywords:
Authors
MORTEZA GHADIMI
Advanced Materials and Nanotechnology Research Center, Faculty of Mechanical Engineering, KN. Toosi University of Technology, Vanak Square, Tehran, Iran
ALI SHOKUHIFAR
Advanced Materials and Nanotechnology Research Center, Faculty of Mechanical Engineering, K.N. Toosi University of Technology, Vanak Square, Tehran, Iran
ASHKAN ZOLRIASATETN
Advanced Materials and Nanotechnology Research Center, Faculty of Mechanical Engineering, KN. Toosi University of Technology (KNTU), Wanak Square, Tehran, Iran