Study of milling effect on particle size and mechanical properties ofWC-Co composite

Publish Year: 1395
نوع سند: مقاله کنفرانسی
زبان: English
View: 367

This Paper With 7 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

NCNNN01_142

تاریخ نمایه سازی: 4 مهر 1396

Abstract:

The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratio by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350 ̊C at a rate of temperature rise 50 ̊C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly full dense was obtained for sample. The calculated mechanical properties revealed optimum amounts of 14.25 GPa hardness, 772 MPa bending strength and 13.86 Pa.m1/2 fracture toughness. The XRD analysis indicated the dominant indentified phases was WC. The FESEM observation showed presence of Co between ceramic particles as binder.

Authors

Ali Fazili

MSc, Materials and Energy Research Center, Karaj, Iran

Leila Nikzad

Assistant Professor, Materials and Energy Research Center, Karaj, Iran