Investigation of performance and compatibility of cement -based polymer - modified cement -based repair concrete
Publish place: 7th International Congress on Civil Engineering
Publish Year: 1385
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,771
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCE07_620
تاریخ نمایه سازی: 29 دی 1384
Abstract:
This study was conducted to evaluate the mechanical properties of repair concretes: a cement based mix, a cement –based mix incorporating silica fume and a polymer modified – cement – based mix. Mechanical properties, such as compressive and tensile strength, elastic modulus and drying shrinkage were determined. Furthermore, the bonding characteristics of repair concrete to substrate were measured by three different tests, including splitting bond test, slant shearing test and direct tensile test. The maximum compressive tensile and direct and splitting bonding strengths were observed for the silica fume incorporating mix. However , the shear bond strength of polymer- modified cement- based, concrete was higher than that of others. With regards to modulus of elasticity, the mix containing silica fume had the highest value among the three repair mixes. The latex modified mix had the lowest value of elastic modulus and the most compatible with the substrate concrete in this regard.
The latex modified mix had significantly lower drying shrinkage value than the other mixes which is considered advantageous in repair applications.
Keywords:
cement-based and polymer-modified cement-based concrete repair concrete , compatibility
Authors
A.R.Bagheri
Assistant prof
S.Hashemi
Research Assistant
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :