Assessment of optimal conditions in centrifugally cast of Aluminum-Brassbimetal composite
Publish place: 4th Iran Aluminum International Conference IIAC2016
Publish Year: 1395
نوع سند: مقاله کنفرانسی
زبان: English
View: 517
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC04_015
تاریخ نمایه سازی: 22 دی 1396
Abstract:
Excellent corrosion resistance and long working life have caused bimetal composites find more usage in different fields such as marine and automotive industries. In this study, pure aluminum melt which is lighter and cheaper compared to brass, was centrifugally cast into the brass bush known as a corrosion resistance shell. To achieve acceptable component, at first, brass bushes were preheated at various temperature between 100-400 °C and then aluminum melt with 1.5 and 2.5 melt-to-solid volume ratio was cast into cylindrical bush rotating at 800, 1600, and2000 (rpm), respectively. Obtained samples were studied using X-ray diffraction analysis (XRD), optical microscope (OM), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and Image J software. Metallurgical joint is probably due to particular dissolving condition that is provided by multiple mechanical forces involved and also possible solid diffusion at the end of solidification process
Keywords:
Authors
Morteza Gholami
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, P.O. Box: ۱۶۸۴۶-۱۳۱۱۴, Iran
Mehdi Divandari
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, P.O. Box: ۱۶۸۴۶-۱۳۱۱۴, Iran
Mohammad-Taghi Salehi
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, P.O. Box: ۱۶۸۴۶-۱۳۱۱۴, Iran