Saeed Farahany - Department of chemical and Materials Engineering, Buein Zahra Technical University, Qazvin

In this study microstructure, phase evolution and solidification characteristics of Zn-0.5%Al-0.5%Mg-0.1%Sb cast alloy have been investigated by non-equilibrium thermal analysis. This alloy was selected as a test case since it is widely used for hot dipping process. Four different peaks related to dissimilar phase evolutions were identified with analyzing corresponding first derivative cooing curve and second derivative cooling curve. Solidification of the quaternary alloy completed in the range of 82.8 °C within 1080.4 s with solidification rate of 0.08 °C/s. Coherency of Zn dendrites occurred at 405.6°C. Solid fraction at coherency point was around 27%. Monitoring solidification of alloy by this method is a rapid, inexpensive and easy to operate compare to other technique in order to investigate microstructure of hot-dipped coating alloy.

Zinc alloy, Solidification, Antimony, Microstructure, Thermal analysis