Kinetic Study of Nickel Leaching from Spent Catalyst in Sulfuric Acid solution
عنوان مقاله: Kinetic Study of Nickel Leaching from Spent Catalyst in Sulfuric Acid solution
شناسه ملی مقاله: CHEMISTRYMED01_031
منتشر شده در همایش ملی یافته های نوین شیمی در صنعت پزشکی در سال 1388
شناسه ملی مقاله: CHEMISTRYMED01_031
منتشر شده در همایش ملی یافته های نوین شیمی در صنعت پزشکی در سال 1388
مشخصات نویسندگان مقاله:
Ahmad Jamshidi Bonab - Department of Applied Chemistry, Islamic Azad University, Ghaemshahr, Iran
S Aahmad Hosseini - Department of Chemical Engineering, Islamic Azad University, Ghaemshahr, Iran
M.Ali. Khalilzade - Department of Applied Chemistry, Islamic Azad University, Ghaemshahr, Iran
خلاصه مقاله:
Ahmad Jamshidi Bonab - Department of Applied Chemistry, Islamic Azad University, Ghaemshahr, Iran
S Aahmad Hosseini - Department of Chemical Engineering, Islamic Azad University, Ghaemshahr, Iran
M.Ali. Khalilzade - Department of Applied Chemistry, Islamic Azad University, Ghaemshahr, Iran
The kinetics of spent nickel oxide catalyst (NiO/Al2O3) leaching in sulfuric acid solution was investigated. The effects of spent catalyst particle size, acid concentration and reaction temperature on Ni extraction rate were determined. The results obtained show that extraction of about 96% is achieved using 200 mesh spent catalyst particle size at a
reaction temperature of 100C for 360 min reaction time with 60% sulfuric acid concentration. The solid/liquid ratio was maintained constant at 1:20 g/ml. Leaching kinetics are controlled either by diffusional mass transfer of either reactant or product ions through a liquid boundary layer or a product metal deposit. The leaching kinetics indicates that chemical reaction at the surface of the particles is the rate-controlling process during the reaction. The activation energy was determined as about 33.65 kJ/mol. This is consistent with values of activation energies reported for surface controlled reactions.
کلمات کلیدی: Spent catalyst – Leaching - Sulfuric acid - kinetic study