CTAB effect on highly electrocatalysis of formaldehyde oxidation based on nickel particles electrodeposited into poly (m-toluidine) film on carbon paste electrode in alkaline medium
عنوان مقاله: CTAB effect on highly electrocatalysis of formaldehyde oxidation based on nickel particles electrodeposited into poly (m-toluidine) film on carbon paste electrode in alkaline medium
شناسه ملی مقاله: PEEL03_024
منتشر شده در سومین همایش پیل سوختی ایران در سال 1388
شناسه ملی مقاله: PEEL03_024
منتشر شده در سومین همایش پیل سوختی ایران در سال 1388
مشخصات نویسندگان مقاله:
Jahan-Bakhsh Raoof - Electroanalytical Chemistry Research Laboratory, Faculty of Chemistry, Mazandaran University, Babolsar, Iran
Mohammad Ali Karimi - Department of Chemistry, Faculty of Science, Payame Noor University (PNU), Sirjan,Iran,E-mail address:ma.karimi۴۳@gmail
Sima Mangelizade
Sayed Reza Hosseini
خلاصه مقاله:
Jahan-Bakhsh Raoof - Electroanalytical Chemistry Research Laboratory, Faculty of Chemistry, Mazandaran University, Babolsar, Iran
Mohammad Ali Karimi - Department of Chemistry, Faculty of Science, Payame Noor University (PNU), Sirjan,Iran,E-mail address:ma.karimi۴۳@gmail
Sima Mangelizade
Sayed Reza Hosseini
This research is aimed to increase the activity of anodic catalysts for formaldehyde electrooxidation. The electrocatalytic oxidation of formaldehyde on nickel particles electrodeposited into poly (m-toluidine) film on carbon paste electrode in the absence and presence of cetyltrimethyl ammonium bromide (CTAB) has been investigated. And The general electrochemical behavior was characterized by cyclic voltammetry in alkaline media. In alkaline medium (i.e. NaOH 0.1 M) a good redox behavior of Ni ()/Ni () couple at the surface of Ni/poly (m-toluidine) modified carbon paste electrode (Ni/PMT/MCPE) in (Ni/CTAB-PMT/MCPE) system can be observed. The results show that Ni/CTAB-PMT/MCPE system exhibits a significant electrocatalytic activity towards oxidation of formaldehyde.