m chegini - School of Metallurgy and Materials Science, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran.
m.r aboutalebi - Center of Excellence for Advanced Materials and Processing (CEAMP), School of Metallurgical and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran.
s.h Seyedein - Center of Excellence for Advanced Materials and Processing (CEAMP), School of Metallurgical and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran.
g.r Ebrahimi - Materials and Polymers Engineering Department, Faculty of Engineering, Hakim Sabzevari University, Sabzevar, Iran.

The hot deformation behavior of a typical martensitic stainless steel containing 2.1% Ni was investigated by means of the compression test in the strain rate range of 0.001-1 s-1 and temperature range of 950-1150 °C. The flow behavior of the steel was evaluated using the flow stress curves and flow-softening map as well as microstructural investigation. The Z and Q maps were plotted as a function of the strain rate and the strain taking into account the strain effect on the hot deformation behavior. In order to obtain the optimum hot deformation regime, the m-map was constructed. It was found out that all restoration mechanisms i.e. dynamic recovery and dynamic recrystallization phenomena take place at different hot working conditions. It was also found out that the dominant softening mechanism at different hot deformation domain depends upon Z parameter. According to the flow curves and also Z, Q, and m maps, the optimum hot deformation conditions have been obtained as: strain range of 0.25-0.5, temperature range of 1000-1100 °C, and strain rate of 0.01-0.1 s-1.

Martensitic stainless steel, Flow curves, Processing maps, Strain effect