Carbon ceramic electrode, a new electrode substrate, was prepared by sol-gel procedure and used for the electropolymerization of aniline and dispersion of platinum nanoparticles into the resulting polyaniline (PANI) film. Aniline monomers were polymerized on carbon ceramic electrode by cyclic voltammetry between -0.2 and 1 V (vs. SCE). Then its surface was potentiostatically coated with Pt nanoparticles at -0.2 V (vs. SCE) in an aqueous solution of 0.1 M H2SO4 containing 2 mM H2PtCl6. The electrocatalytic oxidation of methanol at this modified electrode (CCEٍٍ|PANI|Pt) has been investigated by cyclic voltammetry in a 0.4 M methanol + 0.3 M H2SO4 solution as supporting electrolyte. The presence of polyaniline film significantly enhances the catalytic oxidation of methanol on carbon ceramic electrode. The effects of various parameters on the electrooxidation of methanol such as, thickness of the polymer film, amount of platinum loadings, medium temperature, working potential limit in anodic direction, and potential scan rate were investigated.

Carbon ceramic electrode, Methanol, Platinum, Nanoparticles, Polyaniline