Evaluation of Cr2O3 Oxide Thickness at Presence of MnFe2O4 Nano Spinel Coating
عنوان مقاله: Evaluation of Cr2O3 Oxide Thickness at Presence of MnFe2O4 Nano Spinel Coating
شناسه ملی مقاله: NAYRC02_046
منتشر شده در دومین همایش ملی نانو مواد ونانوتکنولوژی در سال 1389
شناسه ملی مقاله: NAYRC02_046
منتشر شده در دومین همایش ملی نانو مواد ونانوتکنولوژی در سال 1389
مشخصات نویسندگان مقاله:
H Ebrahimifar - Post graduate student, Department of Material Science and Engineering, Shahid Bahonar University of Kerman
M Zandrahimi - Associate Professor, Department of Material Science and Engineering, Shahid Bahonar University of Kerman
خلاصه مقاله:
H Ebrahimifar - Post graduate student, Department of Material Science and Engineering, Shahid Bahonar University of Kerman
M Zandrahimi - Associate Professor, Department of Material Science and Engineering, Shahid Bahonar University of Kerman
Ameliorating the performance of solid oxide fuel cells (SOFCs) is one of the challenges in this field. The goal of this study was to coat AISI 430 ferritic stainless steel which uses as interconnect in a manganese-base pack mixture by pack cementation method. During oxidation tests the coating layer converted to the Mn3O4 spinel and MnFe2O4 nano spinel. Isothermal oxidation, cyclic oxidation and oxidation at different temperatures (400-900 ºC) were applied to evaluate the oxide layer thickness which was created during these tests. Results showed that in eachtest, the formed spinels reduced the chromia growth compared with uncoated ones
کلمات کلیدی: Solid oxide fuel cell, AISI 430 ferritic stainless steel, Spinel, Oxidation,Oxide thickness