Mojtaba Farrokhi - Polymer Reaction Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University, P.O. Box: ۱۴۱۱۵-۱۱۴, Tehran, I.R. Iran
Mahdi Abdollahi - Polymer Reaction Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University, P.O. Box: ۱۴۱۱۵-۱۱۴, Tehran, I.R. Iran

Polystyrene (PSt) has been known as one of the important polymers with a wide range of applications. Ability to synthesize PSt with different but predictable molecular weights for various applications is very important in the laboratories and industries. In this study, using various simple and inexpensive techniques with only free radical mechanism, it was tried to synthesize PSt with different low (< 2×104 g mol-1) to high (> 105 g mol-1) molecular weights. PSts with high and moderate molecular weights (2×104-105 g mol-1) were synthesized using thermal and conventional free radical polymerizations, respectively. Reverse iodine transfer radical polymerization (RITP) was utilized to synthesize PSt with a low and controlled molecular weight. Conversion, molecular weight distribution and PSt structure were analyzed using 1H-NMR spectroscopy and size exclusion chromatography (SEC), respectively. Moreover, ω-iodo poly(dimethylsiloxane), i.e. PDMS-I, was also used as a macrotransfer agent for ITP of styrene. Diblock copolymer of PDMS-b-PSt was characterized by 1H-NMR and SEC analyses.

Polystyrene, low to high molecular weights, thermal polymerization (TP), free-radical polymerization, (reverse) iodine transfer radical polymerization ((R)ITP)