Evaluation of Surface Characteristic Changes of WaveOne Gold and WaveOne Single Reciprocating Files Using Scanning Electron Microscopy: An in-vitro Study
Publish place: Journal of Dental Materials and Techniques، Vol: 7، Issue: 1
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 250
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-7-1_004
تاریخ نمایه سازی: 18 تیر 1398
Abstract:
Introduction: The purpose of this study was to evaluate surface topography of WaveOne Gold (WOG) and WaveOne (WO) files using SEM before and after use. Methods: Twelve primary files from each system were scanned for surface defects before instrumentation at 100x and 750x. Each file was planned ti be used to instrument six root canals and then examined under SEM after preparing one, three and six canals at same magnifications. Data were scored and statistically analyzed using Mann Whitney and Friedman tests (p≤ 0.05). Results: Surface defects were detected in both study groups with higher values in WOG group before use. Surface defects significantly increased in both WO and WOG groups after use. WOG group showed significantly greater defects including metal strips, pitting, craters, micro-cracks and blunt edges (p≤ 0.05). Conclusion: WaveOne Gold file has a different metallurgy due to it’s gold finish that does not enhance it’s resistance to surface defects during clinical use.
Keywords:
Authors
Ahmed Menecy
BDS, Department of Conservative Dentistry, Alexandria University, Egypt
Nayera Mokhless
PhD, Professor of Endodontics, Department of Conservative Dentistry,Alexandria University, gypt
Seham Hanafy
PhD, Professor of Biomaterials, Department of Dental Biomaterials, Alexandria University, Egypt
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :