Effect of Storage Media and Sterilization Method on Shear Bond Strength of Composite to Enamel of Extracted Teeth
Publish place: Journal of Dental Materials and Techniques، Vol: 6، Issue: 3
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 285
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-6-3_001
تاریخ نمایه سازی: 18 تیر 1398
Abstract:
Aim: To evaluate the effect of storage media and autoclaving on shear bond strength of composite to enamel. Materials and Methods: 100 human premolars were randomly divided into ten groups of ten as follows: C: freshly extracted teeth. A: Autoclaved freshly extracted teeth. CH-6: 6 month storage in 0.5 % chloramine T. CA-6: 6 month storage in 0.5 % chloramine T + autoclaving. T-6: 6 month storage in 0.04 % thymol. TA-6: 6 month storage in 0.4% thymol + autoclaving. Ch-12:12 month storage in 0.5 % chloramine T. CA-12: 12 month storage in 0.5 % chloramine T + autoclaving. T-12: 12 month storage in 0.4% thymol. TA-12:12 month storage in 0.4% thymol + autoclaving. One composite cylinder was bonded on each specimen for evaluation of shear bond strength (SBS) and failure modes. Data were analyzed using three-way ANOVA, Tukey’s post hoc and Chi square tests and the level of significance was set at P= 0.05. Results: Autoclaving and storage media had no significant effect on SBS (P-value = 0.818 for storage media and P-value = 0.221 for autoclaving). However, storage duration significantly changed SBS (P-value = 0.00). There were no correlations among the variables (P-value > 0.05). Storage media and duration had no significant effect on failure modes (P-value > 0.05), but autoclaving significantly increased cohesive failure of enamel (P-value =0.039). Conclusion: Storage of teeth in chloramine T and thymol had no significant effect on bond strength to enamel. Although autoclaving of specimens may not alter bond strength, it can significantly increase the cohesive failure of enamel.
Keywords:
Authors
Alireza Boruziniat
Dental Materials Research Center, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran
Nasrin Danaifard
general dentist
Mahshid Gifani
Post-graduate student, Department of Pediatric Dentistry, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran
Narjes Hakimi
Post-graduate student, Department of Operative Dentistry, School of Dentistry, Mashhad University of Medical Sciences, Mashhad, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :