Effects of Shielding Gas on the Mechanical and Microstructural Properties of 409L Ferritic Stainless Steels during Gas Metal Arc Welding
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 330
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-1-2_005
تاریخ نمایه سازی: 25 تیر 1398
Abstract:
The present study investigates the effects of type of shielding gas on the weld microstructure and mechanical properties of 409L ferritic stainless steel. For this purpose, Ar, Ar +20% He, Ar + 12% CO2, and Ar + 25% CO2 were used as shielding gases in gas metal arc welding (GMAW) of stainless steel. To evaluate the welds, non-destructive inspections of the specimens were followed by mechanical (hardness and tensile) tests while microstructural examinations of both the heat affected zone (HAZ) and the fusion zone were performed. Moreover, the phases produced were observed and identified by analyzing the specimens using SEM and EDS techniques. Results showed that specimens welded with Ar + 25% CO2 and Ar + 12% CO2 have the highest strength and hardness values in the fusion zone due to the formation of martensite around the ferrite grains. However, the enhancements observed in the mechanical properties of specimens welded with Ar and Ar +20% He were attributed to the reduced ferrite grain size and martensite content
Keywords:
Ferritic Stainless Steels , Shielding Gas , Gas Metal Arc Welding , Microstructure , Mechanical Tests
Authors
A. Feghhi
Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran.
A. Emamikhah
Department of Mechanical Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran.
Y. Bayat Asl
Department of Mechanical Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :