Investigation of martensite particles distribution on strain localization in dual phase steels using SEM examination as well as crystal plasticity simulation
عنوان مقاله: Investigation of martensite particles distribution on strain localization in dual phase steels using SEM examination as well as crystal plasticity simulation
شناسه ملی مقاله: ISME24_757
منتشر شده در بیست و چهارمین کنفرانس سالانه بین المللی انجمن مهندسان مکانیک ایران در سال 1398
شناسه ملی مقاله: ISME24_757
منتشر شده در بیست و چهارمین کنفرانس سالانه بین المللی انجمن مهندسان مکانیک ایران در سال 1398
مشخصات نویسندگان مقاله:
Mohammad Jafari - Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran;
Saeed Ziaei-Rad - Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran;
Navid Saeido - Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Mostafa Jamshidian - Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran
خلاصه مقاله:
Mohammad Jafari - Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran;
Saeed Ziaei-Rad - Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran;
Navid Saeido - Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Mostafa Jamshidian - Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran
The morphology of the dispersed martensite islands between ferrite phases has a key role in formation shear bands of dual phase steels. In this study, the relationship between strain localization regions and the formation of shear bands with martensite dispersion was investigated for fine-grained DP 780 steel by using experimental observation and numerical simulation. SEM studies of the deformed structure showed that voids nucleated at ferritemartensite interface within larger ferrite grains and lower local martensite fraction. This is believed to be mainly due to the higher shear deformation ability of the larger ferrite grains and the less uniform strain distribution within the larger ferrite grains compared to the smaller ones. These results were analyzed precisely with crystal plasticity finite element method and the correlation between shear bands and microstructure-level inhomogeneity was identified.