Microstructure of spark plasma sintered TiB2 and TiB2–AlN ceramics
Publish place: Advanced Ceramics Progress، Vol: 5، Issue: 1
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 507
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-5-1_006
تاریخ نمایه سازی: 23 مهر 1398
Abstract:
In this research study, the effects of aluminum nitride (AlN) additive on the densification behavior and microstructure development of titanium diboride (TiB2) based ceramic matrix composite were investigated. In this way, a monolithic TiB2 ceramic and a TiB2–5 wt% AlN ultrahigh temperature ceramic composite were fabricated by spark plasma sintering (SPS) process at a temperature of 1900 °C for a dwell time of 7 min under an externally applied pressure of 40 MPa in vacuum conditions. The relative density measurements were carried out using the Archimedes principles for evaluation of bulk density and rule of mixtures for calculation of theoretical one. Compared to the additive-free monolithic TiB2 ceramic sample with a relative density of ~96%, the addition of AlN as a sintering aid greatly improved the sinterability of TiB2 matrix composite so that a near fully dense sample with a relative density of ~100% were obtained by the spark plasma sintering process. The removal of harmful oxide impurities of titania (TiO2) and boria (B2O3) from the surfaces of starting TiB2 powder particles and in-situ formation of new phases such as aluminum diboride (AlB2) and Al2Ti as an intermetallic compound of aluminum and titanium, not only improved the sinterability of the composite ceramic, but also significantly prevented the extreme growth of TiB2 grains.
Keywords:
Authors
Zohre Ahmadi
Ceramic Department, Materials and Energy Research Center (MERC), Karaj, Iran
Zahra Hamidzadeh Mahaseni
Department of Mechanical Engineering, University of Mohaghegh Ardabili, Ardabil, Iran
Mohammad Dashti Germi
Department of Mechanical Engineering, University of Mohaghegh Ardabili, Ardabil, Iran
Mehdi Shahedi Asl
Department of Mechanical Engineering, University of Mohaghegh Ardabili, Ardabil, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :