Formation of nanograin in IF steels by friction stir processing
عنوان مقاله: Formation of nanograin in IF steels by friction stir processing
شناسه ملی مقاله: ICME11_133
منتشر شده در یازدهمین کنفرانس ملی مهندسی ساخت و تولید ایران در سال 1389
شناسه ملی مقاله: ICME11_133
منتشر شده در یازدهمین کنفرانس ملی مهندسی ساخت و تولید ایران در سال 1389
مشخصات نویسندگان مقاله:
A. Chabok - Ms. Student, Faculty of Mining and Metallurgical Engineering, Amirkabir university of technology
K. Dehghani - Associate Professor, Faculty of Mining and Metallurgical Engineering, Amirkabir university of technology
M. Mazinani - Ms. Student, Faculty of Mining and Metallurgical Engineering, Amirkabir university of technology
خلاصه مقاله:
A. Chabok - Ms. Student, Faculty of Mining and Metallurgical Engineering, Amirkabir university of technology
K. Dehghani - Associate Professor, Faculty of Mining and Metallurgical Engineering, Amirkabir university of technology
M. Mazinani - Ms. Student, Faculty of Mining and Metallurgical Engineering, Amirkabir university of technology
An IF steel was subjected to friction stir processing using a carbidetungsten pin with the diameter of 16 mm. The rotating speed of pin was 1600rpm, whereas, the applied traverse speed was 31.5mm/min. The specimens were water quenched immediately after the FSP. The results show that the FSP of IF steel resulted in the formation of a 30-35 μm thick surface layer with the nanograins of 50-125 nm. There was a continuous decrease in the hardness from the nanograin surface layer towards the center of specimen. There was almost a three-fold increase in the hardness.
کلمات کلیدی: Nanograin IF steel; Nanostructure materials; FSP