Effect of Submerged Arc Welding Parameter on Crack Growth Energy on St37
Publish place: Journal of Solid Mechanics، Vol: 9، Issue: 4
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 258
This Paper With 13 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JSMA-9-4_015
تاریخ نمایه سازی: 12 اسفند 1398
Abstract:
In this article the influence of welding parameters such as electrical current, feed rate and stick out on crack growth energy was investigated. Therefore, prepared specimens were welded in various conditions. Using the Minitab software, 18 states of 36 possible states were chosen and applied. Then a crack was crated on the weld metal and the force-displacement diagram was plotted. Comparison of results shows that in high electricity current, the extra heat flux is the dominant factor, which causes coarse grains of microstructures. On the other hand, in low electricity current, lack of fusion and penetration reduce the crack propagation energy. Furthermore, the neural network could predict the amount of energy with high accuracy.
Keywords:
Authors
J.A Khodaii
Department of Mechanical Engineering ,Amirkabir University of Technology, Tehran, Iran
A Mostafapour
Department of Mechanical Engineering ,University of Tabriz, Tabriz, Iran
M.R Khoshravan
Department of Mechanical Engineering ,University of Tabriz, Tabriz, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :