CTAB synthesis of vanadium oxide nanorods prepared by simple Chemical method
Publish place: دومین کنفرانس بین المللی علوم و مهندسی
Publish Year: 1394
نوع سند: مقاله کنفرانسی
زبان: English
View: 553
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICESCON02_209
تاریخ نمایه سازی: 16 شهریور 1395
Abstract:
In this paper, structural and morphological properties of vanadium oxides (V2O5) nanoparticles have been studied. V2O5 nanoparticles were synthesized using a simple chemical method by sodium metavanadate as precursor and Cetyl trimethylammonium bromide (CTAB) as surfactant. The samples were characterized by high resolution transmission electron microscopy (HRTEM), field effect scanning electron microscopy (FESEM) and X-ray diffraction (XRD). As there are many forms of vanadium oxides produced during this process, x-ray diffraction (XRD) technique was used to identify V2O5 phase. particles was around 5 nm as estimated by HRTEM technique and average diameter of annealed nanorods was around 9 nm as estimated by XRD technique and direct FESEM observation. The surface morphological studies from SEM depicted that nanorods were appeared after annealing process. The effect of CTAB surfactant on the particle morphology was also studied and the results show that the CTAB can reduce the particle size of nanorods to less than 10 nm.
Keywords:
Authors
Majid Farahmandjou
Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, Iran
Niloufar Abaeyan
Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, Iran
Tahereh Pormirjafari Firoozabadi
Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :