Synthesis of alumina-mullite nanopowder using AlCl3.6H2O & colloidal silica via Sol–gel method
Publish place: 2nd International Conference on Composites: Characterization, Fabrication and Application
Publish Year: 1389
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,335
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT02_042
تاریخ نمایه سازی: 24 مهر 1389
Abstract:
Via sol-gel method, it can be obtained, the homogeneous distribution of mullite in alumina matrix. In this work, alumina-mullite nanopowder was synthesized by aluminium chloride hexahydrate and colloidal silica via sol-gel method and in the other works it had been prepared by alumina and TEOS. According to the XRD patterns of alumina-mullite 15%vol. precursors calcined at different temperatures, transitional alumina (γ, κ) & silica phases (quartz, tridymite) crystallize at around 900°C. Then it transforms to α alumina & mullite in the range of 1000-1300°C completely. Specific surface area and density of the nanopowder calcined at 900oC are 105.4 ± 0.4 m2/g & 3.646 ± 0.007 g/cm3 respectively. Then the nanopowder was observed by TEM.
Keywords:
Authors
A Sedaghat
Ph.D. student
E aheri-Nassaj
Professor, Department of Materials Science and Engineering, Tarbiat Modares University
G.D Soraru
,۳Professor, Departmentof Materials Engineering and Industrial Technology, University of Trento
R Ceccato
Professor, Materials & Energy Research Centre, PO Box ۱۴۱۵۵-۴۷۷۷, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :