Effect of process parameters on tensile strength of welds and modeling of laser welding of PA6/NBR/clay nanocomposite by response surface methodology
Publish place: Polyolefins Journal، Vol: 7، Issue: 2
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 498
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-7-2_004
تاریخ نمایه سازی: 15 مرداد 1399
Abstract:
Polyamide 6 / nitrile butadiene rubber / nanoclay (PA6/NBR/clay) nanocomposite has gathered wide acceptance in industry. Laser welding, as a fabrication method, is applied to welding of polymer nanocomposites. In this study, the input parameters (clay (Closite 30B) content, laser power, scan velocity and stand-off-distance) are varied to achieve the best responses (tensile strength of welds). Response surface methodology (RSM) is utilized to investigate the effect of input parameters on mechanical properties. Morphology and tensile properties of nanocomposites were observed with scan electron microscopy (SEM), transmission electron microscopy (TEM) and tensile test. The results demonstrated that increasing the clay content from 1 to 5%wt and stand-off-distance from 4 to 8 mm decreased tensile strength of welds about 15% and 5%, respectively. The tensile strength of PA6/NBR composite is 25.6, whereas the prediction models showed that under optimal conditions of laser power of 105 W, scan velocity of 300 mm/min and stand-off-distance of 4 mm, the maximum tensile strength of PA6/NBR nanocomposite with 1, 3 and 5 % nanoclay are 27.2 MPa, 27.6 MPa and 24.7 MPa, respectively. These tensile strengths are about 99, 89 and 73% of the strength of these nanocomposites before welding.
Keywords:
Authors
Moammadreza Nakhaei
Faculty of Mechanics and Energy, Shahid Beheshti University, Tehran, Iran
Ali Ahmadi
Faculty of Mechanical Eng., Shahid Rajaee Teacher Training University, Tehran, Iran
Ghasem Naderi
Iran Polymer and Petrochemical Institute, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :