Synthesis and Characterization of Co-doped CeO2 Ceramic Electrolyte for IT-SOFC
Publish place: Iranian Journal of Hydrogen & Fuel، Vol: 6، Issue: 2
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 247
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJHFC-6-2_005
تاریخ نمایه سازی: 5 شهریور 1399
Abstract:
Solid oxide fuel cells are electrochemical systems. One of the most important compounds in their structure is the ceramic electrolyte. The ceramic electrolyte property of the CeO2 compound is currently being investigated in many studies. In this study, we tried to synthesize different CeO2 compounds. Ce0.85-x-yLaxGdyO2 nanocrystalline powders were prepared via the hydrothermal method. Phases identification was completed through X-ray diffraction, SEM-EDS, thermal and impedance analysis. XRD data showed that all the obtained powders had a cubic fluorite structure. After examining the surface images, it was seen that the particle sizes were on the micron scale. Impedance measurements of the pelletized sample were also made. The Ce0.85-x-yLaxGdyO2 powder was sintered at 1250 °C. Increased conductivity value was calculated with increasing temperature. The best conductivity was observed at 750 oC and the conductivity value was 0.0022 S.cm-1. The results indicated that the degree of electrical conductivity was found to be low regarding the applications in intermediate temperature solid oxide fuel cells.
Keywords:
Authors
Handan ÖZlLÜ TORUN
Department of Energy System Engineering, Kahramanmaras İstiklal University, Kahramanmaras/Turkey
Rabia KIRKGEÇİt
Institute of Science, Material Science and Engineering, ۱KahramanmaraşSütçü İmam University,Kahramanmaraş, ۴۶۰۵۰, Turkey
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :