Electrodeposition of Ni-P/Ni-Co bilayer coating on St37 steel
Publish Year: 1399
نوع سند: مقاله کنفرانسی
زبان: English
View: 307
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CARSE05_001
تاریخ نمایه سازی: 17 آذر 1399
Abstract:
The surface characteristics of engineering components determine their durability and performance during the service condition. The goal of this investigation is to study the effect of applied current density on microhardness of the Ni-P/Ni-Co bilayer coating. Both Ni-P interlayer and Ni-Co top layer were electrodeposited using direct current (DC). The Ni-P layer was electrodeposited on polished St37 steel substrates followed by deposition of Ni-Co at various current densities, i.e., 4-6 A dm-2. The Vickers microhardness tester was used to evaluate the microhardness of the electrodeposited coatings. Results show that the applied current density has a significant influence on microhardness of the bilayer coating, where increasing current density from 4 to 5 A dm-2 leads to a 34 HV increment in the microhardness value. Note that further increase in the current density inversely affect the mechanical properties
Keywords:
Authors
Saman Safavi
Master of Science, University of Tabriz, Tabriz, Iran
Ali Rasooli
Associated professor at University of Tabriz, Tabriz, Iran