The Effect of Zircon on Long-Time Corrosion Resistance of Alumina
Publish place: Advanced Ceramics Progress، Vol: 3، Issue: 4
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 198
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-3-4_007
تاریخ نمایه سازی: 11 اردیبهشت 1400
Abstract:
Corrosion resistance of zircon reinforced alumina refractories has been carried out through static crucible test. The corrosion measurements with percentage, the penetration depth of molten steel and the microstructure of the refractories were evaluated after soaking ۱۵۰ h at the temperature of ۱۵۰۰˚C. Results showed that the corrosion resistance of alumina increased by adding ۲۰ wt% zircon, and decreased with further increasing of zircon. Also, the samples containing ۲۰ wt% of zircon obtained the minimum porosity. Microstructural features of this composite showed needle-like mullite grains and higher amount of zirconia particles which may be responsible for providing the corrosion resistance to melt penetration.
Keywords:
Authors
Rana Nasrollahnezhad
Ceramic Department, MERC
Hudsa Majidian
Materials Energy Research Center
Leila Nikzad
Materials and Energy
Touraj Ebadzadeh
Ceramic , Merc
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :