Effect of Welding Parameters on Microstructure and Mechanical Properties of Friction Stir Spot Welded of Titanium Alloy TiAl۶V۴
Publish place: International Journal of Advanced Design and Manufacturing Technology، Vol: 9، Issue: 2
Publish Year: 1395
نوع سند: مقاله ژورنالی
زبان: English
View: 276
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-9-2_011
تاریخ نمایه سازی: 18 اردیبهشت 1400
Abstract:
In this study, friction stir spot welding (FSSW) is applied to join the TiAl۶V۴ titanium alloy with ۱.۵ mm thickness and then the effect of rotational speed and tool dwell time on microstructure and mechanical properties is investigated. In this regard, the speed of the tool rotation was considered as ۸۰۰, ۱۰۰۰, and ۱۲۰۰ rpm, as well as the tool dwell time was set at ۷ and ۱۲s. Microstructural evaluation was carried out using optical microscopy (OM) and scanning electron microscopy (SEM). In addition, tensile-shear and hardness studies were performed to analyze mechanical properties. The obtained results from microstructural evaluation show that the welded joints consist of two regions, namely the SZ and the HAZ-regions. Additionally, microstructure of the SZ-region was identified in the form of α/β layer within the initial β-phase. The results of tensile/shear tests and micro-hardness test indicated that the joint strength and hardness are enhanced with increasing the rotational speed and dwell time. The tensile/shear strength is increased from ۲.۷ to ۱۵ KN with increasing the rotational speed at constant dwell time of ۷s, and also is increased from ۷.۳ to ۱۷.۲۵ KN with increasing the rotational speed at constant dwell time of ۱۲s. The maximum tensile/shear strength was achieved for the welded joint with the dwell time of ۱۲s and rotational speed of ۱۲۵۰ rpm. The hardness of SZ, HAZ regions and base metal are measured around ۳۸۰ to ۴۲۰, ۳۴۰ to ۳۸۰, and ۳۰۰ to ۳۴۰, respectively.
Keywords:
Authors
Saeid Nader
Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Masoud Kasiri- Asgarani
Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
kamran amini
Department of Mechanical Engineering, Tiran Branch, Islamic Azad University, Isfahan, Iran
Morteza Shamanian
Department of Mechanical Engineering, Isfahan University of Technology, Isfahan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :