Hot Workability and Processing Map of High Gd Content Mg-Gd-Zn-Zr-Nd Alloy
Publish place: The Iranian Journal of Materials Forming، Vol: 8، Issue: 2
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 439
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-8-2_006
تاریخ نمایه سازی: 28 اردیبهشت 1400
Abstract:
Hot workability of as-extruded high Gd content Mg-۵Gd-۰,۵Zn-۰.۵Zr-۲.۵Nd alloy was investigated using the hot compression test in a temperature range of ۳۰۰-۵۰۰ °C and strain rates of ۰.۰۰۱-۱s-۱. Hot workability assessment was conducted by capturing microstructural evolution of high temperature deformed samples, and by constructing power dissipation and instability maps. Using experimental data of hot compression tests, the power dissipation map of the alloy was constructed, in which a domain of dynamic recrystallization (DRX) occurred at the temperature range of ۳۵۰-۴۵۰ °C and strain rate of ۰.۰۰۱-۰.۱ s-۱, representing the optimum hot working window. Furthermore, the processing map of the alloy was constructed, and flow instability regions were also indicated based on the Ziegler's flow instability criterion.
Keywords:
Authors
Sahar Mosadegh
Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran
Mehrdad Aghaie-khafri
Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran
Behzad Binesh
Department of Materials Science and Engineering, University of Bonab, Bonab, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :