Investigation of Microstructure weld zone of Hastelloy X Pulsed Nd-YAG laser welds
Publish Year: 1392
نوع سند: مقاله ژورنالی
زبان: English
View: 153
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-1-4_006
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
In the present study, the microstructure of welded zone of Hastelloy X sheets with thickness of ۱ mm via pulsed Nd-YAG laser welding were studied. This welding process was done by autogenus and conductive method. Microstructure were observed by metallurgical OM and SEM. Results shown Solidification of the weld metal is dendritic. The dendrites in the central zone of the welding are fine and equiaxed while they are larger and columnar in the fusion boundary. Epitaxial growth was observed in the interface of base metal and weld metal. Alloy elements Segregation did not occur during the solidification process and the fine cracks were not observed in the welding zone of the alloy. Micro hardness results indicated that the hardness of welded metal were more than base metal and cause to decrease grain size at welded metal more than base metal. This phenomenon was occurred due to more differences between heating and cooling rate in this welding process.
Keywords:
Authors
Farrokh Najafzadegan
Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran
Hojatallah Mansori
Department of Materials Engineering, Malek-E-Ashtar University, Isfahan, Iran
Morteza shamanian
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :