Inclusion Removal Mechanisms of Al-Killed ۳۰۴ Low Carbon Stainless Steel Melt Using Hercynite Coated Al۲O۳-C Ceramic Foam Filters
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 350
This Paper With 11 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-9-2_003
تاریخ نمایه سازی: 21 مهر 1400
Abstract:
Carbon bonded alumina foam filters have been successfully using for steel melt filtration. Enhancement of the filtration capacity of Al۲O۳-C foam filters is a key factor in order to make them applicable to be used for large steel casting parts or continuous casting of steel. In the present study, filtration performance of hercynite coated carbon bonded alumina foam filters containing ۱ Wt.% of nano-TiO۲ were evaluated by the exposure to an Al-killed ۳۰۴ low carbon stainless steel melt. Successful impingement of steel melt into the filters revealed the filter structure strength and effectiveness under casting temperature and molten metal exposure conditions. Microstructural investigations using a field emission scanning electron microscope (FESEM) equipped with energy dispersive X-ray spectroscopy (EDS) analysis of the active hercynite coated filter surfaces after steel melt filtration revealed the entrapment of the oxide inclusions from the steel melt on the surface of the filter. In addition, filtration mechanisms for whiskers and dendritic Al۲O۳, and hercynite inclusions at different Al/oxygen activity conditions of the steel melt were proposed. To this end, the feasible potential for the application of hercynite coated Al۲O۳-C filters for low and ultra-low carbon steel casting processes could be promising.
Keywords:
Authors
Ali Baghaei
Advanced Materials Research Center, Materials Engineering Department, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Amir Abbas Nourbakhsh
Advanced Materials Research Center, Materials Engineering Department, Najafabad Branch, Islamic Azad University, Najafabad, Iran; Department of Materials Science, Shahreza Branch, Islamic Azad University, Shahreza, Iran
Reza Ebrahimi-Kahrizsangi
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :