Investigation of the viscoelastic properties of anatase TiO2-Polypropylene nanocomposites exposed to UV irradiation
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,274
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PPSRC2011_354
تاریخ نمایه سازی: 30 بهمن 1390
Abstract:
TiO2-Polypropylene nanocomposites containing 0.5 and 1 wt% anatase TiO2 were prepared. Viscoelastic properties of the nanocomposites were investigated via dynamic mechanical thermal analysis (DMTA) before and after UV irradiation. The results reveal that the composites filled with 1wt% nano-titania show a noticeable decrease and increase in storage modulus and damping factor, respectively, indicating more photocatalytic property under UV irradiation
Keywords:
Authors
Saeed Atashdaman
Department of Polymer, Science and Research Branch, Islamic Azad University, Tehran
Mohammad Mehdi Jalili
Department of Polymer, Science and Research Branch, Islamic Azad University, Tehran
Saeed Farrokhpay
The University of Queensland, Brisbane, Australia
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :