Fractographic Aspects of Stress Corrosion Failure of Zircaloy ۲ in CH۳OH HCL Solutions
Publish place: International Journal of Engineering (IJE)، Vol: 3، Issue: 1
Publish Year: 1369
نوع سند: مقاله ژورنالی
زبان: English
View: 174
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-3-1_003
تاریخ نمایه سازی: 18 بهمن 1400
Abstract:
Fracture surface of Zircaloy-۲ specimens tested under constant crosshead speed in CH۳OH/۰.۴ Vol. %HCI solution with and without selenium (۲۵ ppm) addition was studied. Using a combined process of deformation and annealing, coarse grained material was also obtained and examined. Two modes of stress corrosion crack propagation were observed: an intergranular zone caused by stress assisted anodic dissolution, and a transgranular cleavage zone, due to hydrogen absorption.