ModeI fracture toughness of Carbon/glass hybrid comopsite
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 197
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-34-11_005
تاریخ نمایه سازی: 10 اردیبهشت 1401
Abstract:
Mode I fracture toughness of carbon/ glass reinforced polyster hybrid composite was invesitigated expermrntally and numerically by using the cosmos)/m ۲.۶ finite element software (fms) by utulizing the hand laup techniqe)(HLU). The single edge notch bending (SENB) test was developed to evalute the mode l fracture toughness of carbon composites, glass composite and hybrid compodite materials at varuos fiber configurations. Scaning electron microscope (SEM) was used to examine the fracture surface of the hybrid composite material under the effect of mode l loading. the expermental result showed the maximum stress intensity (sif) factor ۸۸۲mpa. mm۱/۲. obtained in the hybrid composite with stacking dequencess (c/g/g/c) during the mode l loading compared to other stacking sequences. this is attributed to the goid interfical between the carbon and glass fibers and matrix face. From the resukts, it was suggested that the expermental results is a goid a gremnent with the finite element modelling
Keywords:
Authors
M. El-Wazery
Department of Production Engineering and Mechanical Design, Faculty of Engineering, Menoufia University, Shebin El-Kom, Egypt
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :