Investigation of Dielectric Properties of Ni/n-TiO۲/p-Si/Al Heterojunction in Wide Range of Temperature and Voltage
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 119
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-35-4_022
تاریخ نمایه سازی: 10 اردیبهشت 1401
Abstract:
In the present study we have investigated the dielectric properties such as dielectric constant (ε'), dielectric loss (ε"), real part of electrical modulus (M'), imaginary part of electric modulus (M") and AC electrical conductivity, (σac) in wide range of applied voltage, temperature and frequency for Ni/n-TiO۲/p-Si/Al heterojunction. A nanocrystalline TiO۲ layer was grown on p-type boron doped silicon in oxygen-controlled environment using optimized KrF excimer laser. Ohmic contact of pure nickel and aluminum metals was made on TiO۲ and silicon respectively, with thermal coating system. The characteristics obtained with the help of conductance-voltage and capacitance-voltage measurements also known as impedance/admittance spectroscopy. The studied parameters are found to be very sensitive to frequency, temperature and voltage. The restructuring and reordering of interface state density due to temperature variations and interfacial polarizations due to frequency variations collectively result the observed changes in the and . With an increase in frequency AC conductivity and electrical modulus also increases. The relaxation mechanism can be observed in the complex electrical modulus analysis. The thermally activated conduction process was indicated by the frequency dependent AC conductivity at different temperatures. Using power law, the AC conductivity was analyzed and found to increase with temperature, applied voltage.
Keywords:
Authors
A. Kumar
Department of Physics and Photonics Science, National Institute of Technology, Hamirpur, India
A. Kumar
Department of Physics, Government College Sujanpur Tihra, India
K. K. Sharma
Department of Physics and Photonics Science, National Institute of Technology, Hamirpur, India
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :