Synthesis of Advanced ZTA for Orthopedic Application by Sol-Gel Method
Publish place: Chemical Methodologies، Vol: 6، Issue: 6
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 172
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CHM-6-6_001
تاریخ نمایه سازی: 19 اردیبهشت 1401
Abstract:
The demand for ceramic products for orthopedic applications is increasing due to the lowest rate of wear. A fourth-generation ceramic (BIOLOX delta; CeramTec.) consists of ۸۲ wt. % Al۲O۳, ۱۷ wt. % (۱.۳ Yttria Stabilized ZrO۲), ۰.۵ wt. % strontium oxide, and ۰.۵ wt. % chromium oxide. It has good mechanical properties compared to the other generations of ceramics (BIOLOX forte and pure alumina), which may increase the range of movement and decrease the rate of dislocation. This ceramic composite (delta) has a smaller grain size (۰.۶ μm) than previous alumina composites (۱.۸ μm). So, this paper tries to obtain the smallest grain size on the scale of nanometers to improve biolox properties and good distribution for its components. By the sol-gel method, the BIOLOX delta was prepared from the gel precursor and sintering at ۱۱۰۰ °C for ۲ h in the oven. The heat-up rate was ۵ °C/min. As-obtained particles were characterized before and after sintering temperature using X-Ray Diffraction (XRD), Energy Dispersive X-Ray Analysis (EDX), and Scanning Electron Microscopy (SEM). The dried powder which was obtained consists of phases, γ-Al۲O۳, θ-Al۲O۳, and δ-Al۲O۳, while ZrO۲ is found as (t + m) ZrO۲ after calcination and the obtained average grain size was (۱۰.۹۴ nm).
Authors
Alaa S. Taeh
Department Materials Engineering, University of Technology, Baghdad, Iraq
Alaa A. Abdul-Hamead
Department Materials Engineering, University of Technology, Baghdad, Iraq
Farhad M. Othman
Department Materials Engineering, University of Technology, Baghdad, Iraq
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :