Assessment of Structure, Dielectric and Gamma-Shielding Properties of Chemically Treated Natural Kaolinitic Clay
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 113
This Paper With 14 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-18-4_006
تاریخ نمایه سازی: 24 بهمن 1401
Abstract:
The structural properties of a natural clay sample (۵۱% kaolinite) were tweaked to suit specific applications. H۲SO۴ and NaOH (۱.۰ M) treatment caused structural alterations and a significant release of Al ions compared to Si ions. Chemical treatment caused structural alterations, according to XRD analysis. FTIR analysis also indicated higher density of polar surface groups upon treatment which affected the corresponding dielectric behaviors. Dielectric measurements shown the suitable application of the materials either as dielectrical insulator and this dependent on the applied frequency. Acid treated kaolinite was reported to be a promising dielectric at ۱۰ and ۱۰۰۰ Hz. With appropriate mass attenuation coefficients (μ/ρ) ۱۲.۰۹۸-۱۲.۱۸۲ cm۲/g and a high half value layer of ۱۰ cm at ۱۰ keV, kaolinite and other treated forms were adequate shielding materials.
Keywords:
Kaolinite , Acid/alkali treatment , Physicochemical characteristics , Dielectric and shielding properties
Authors
Anas Al-Reyahi
Department of Physics, Faculty of Science, The Hashemite University, P.O. Box ۳۳۰۱۲۷, Zarqa ۱۳۱۳۳, Jordan.
Salem Yahya Degs
Department of Chemistry, Faculty of Science, The Hashemite University, P.O. Box ۳۳۰۱۲۷, Zarqa ۱۳۱۳۳, Jordan.
Ayman Issa
Department of Chemistry, Faculty of Science, The Hashemite University, P.O. Box ۳۳۰۱۲۷, Zarqa ۱۳۱۳۳, Jordan
Zyad Khattari
Department of Physics, Faculty of Science, The Hashemite University, P.O. Box ۳۳۰۱۲۷, Zarqa ۱۳۱۳۳, Jordan.
Mohammed Abu Al Sayyed
Faculty of Science, University of Tabuk, Saudi Arabia
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :