Characterization of Nanocrystalline NiP Alloy Coatings Electrodeposited at Various Current Densities

Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 133

This Paper With 7 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

JR_IJMSEI-18-3_010

تاریخ نمایه سازی: 24 بهمن 1401

Abstract:

Nickel phosphorus alloy coatings were prepared by electrodeposition route from sulfate electrolyte bath at various current densities. SEM studies reveal spherical grains covered the entire surface with uniform distribution. EDX results showed a linear increase of P content in the developed deposits with current density and therefore, enhancing the grains size and drop of the hardness values. XRD studies reveal monocrystalline orthorhombic alloys at a low amount of phosphorus (۱۰.۸۸ wt. %). Corrosion tests show that ۱ A.dm-۲ is the best applied current density giving the nobler Ecorr (-۱۷۱.۴ mV) and the lower icorr (۴.۶۴ µA/cm۲).

Authors

Farid Lekmine

Physics laboratory of Thin Layers and Applications, Biskra University,

Hachemi Ben Temam

Physics laboratory of Thin Layers and Applications, Biskra University, BP ۱۴۵ RP, Biskra ۰۷۰۰۰, Algeria

Elhachmi Temam

Physics laboratory of Thin Layers and Applications, Biskra University, BP ۱۴۵ RP, Biskra ۰۷۰۰۰, Algeria

مراجع و منابع این Paper:

لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :
  • Sknar, Y. E., Savchuk, O. O. and Sknar, I. V., ...
  • Chang, L., Chen, C. H. and Fang, H., "Electrodeposition of ...
  • Li, L., Zhang, Y., Deng, S. and Chen, Y., "Effect ...
  • Mahalingam, T., Raja, M., Thanikaikarasan, S., Sanjeeviraja, C., Velumani, S., ...
  • Suzuki, Y., Arai, S. and Endo, M., "Electrodeposition of Ni–P ...
  • Torre, F. D., Swygenhoven, H. V. and Victoria, M., "Nanocrystalline ...
  • Ma, C., Wang, S. C., Wang, L.P., Walsh, F. C. ...
  • He, Y., Wang, S. C., Walsh, F. C., Chiu, Y. ...
  • Saitou, M., Okudaira, Y. and Oshikawa, W., "Amorphous Structures and ...
  • Daly, B. P. and Barry, F. J., "Electrochemical nickel phosphorus ...
  • Ng, P. K., Snyder, D. D., LaSala, J., Clemens, B. ...
  • Balaraju, J. N., Sankara Narayanan, T. S. N. and Seshadri, ...
  • Carbajal, J. L. and White, R. E., "Electrochemical Production and ...
  • Brenner, A., Electrodeposition of Alloys, vol. ۱, Academic Press, New ...
  • Zeller, R. L. and Landau, U., "Electrodeposition of Ni-P Amorphous ...
  • Morikawa, T., Nakade, T., Yokoi, M., Fukumoto, Y. and Iwakura, ...
  • Pillai, A. M., Rajendra, A. and Sharma, A. K., "Electrodeposited ...
  • Murugan, V. K., Jia, Z., Syaranamual, G. J., Gan, C. ...
  • You, Y., Gu, C., Wang, X. and Tu, J., "Electrochemical ...
  • Gu, C. D., Lian, J. G., Li, L. N. and ...
  • Gu, C. D., Lian, J. G., Li, L. N. and ...
  • Gu, C. D., Lian, J. G. and Jiang, Z., "Multilayer ...
  • Ben Temam, H., Chala, A. and Rahmane, S., "Microhardness and ...
  • L Sanches, L. S., Domingues, S. H., Marino, C. E. ...
  • Karayianni, H. S., Batis, G. and Vassiliou P., "Corrosion resistance ...
  • Hung, K. C., Chan, Y. C., Tang, C. W. and ...
  • Sankara Narayanan, T. S. N., Baskaran, I., Krishnaveni, K. and ...
  • Lu, G. and Zangari, G., "Corrosion resistance of ternary Ni-P ...
  • ۲۹ Jang, J. W., Kim, P. G., Tu, K. N., ...
  • نمایش کامل مراجع